INFLUENCE OF THE SOLIDIFICATION PARAMETERS ON DENDRITIC MICROSTRUCTURES IN UNSTEADY-STATE DIRECTIONALLY SOLIDIFIED OF LEAD-ANTIMONY ALLOY

作者：Sahin M; Cadirli E; Kaya H^*

来源：Surface Review and Letters, 2010, 17(5-6): 477-486.

DOI：10.1142/S0218625X10014326

• Dendrites
• Pb-Sb alloy
• microstructures
• solidification
• crystal growth

Pb-9.3wt.%Sb alloy was directionally solidified upwards under argon atmosphere under the two conditions; with different temperature gradients, (G = 0.93-3.67K/mm) at a constant growth rate (V = 17.50 mu m/s) and with different growth rates (V = 8.30-497.00 mu m/s) at a constant (G = 3.67 K/mm) in a Bridgman furnace. The dependence of characteristic microstructure parameters such as primary dendrite arm spacing (lambda(1)), secondary dendrite arm spacing (lambda(2)) and dendrite tip radius (R) on the growth rate (V) and the temperature gradient (G) were determined by using a linear regression analysis. A detailed analysis of microstructure were also made and compared with the theoretical models and similar experimental works on dendritic solidification in the literature.

• 出版日期2010-12