Anisotropic electrical conductivity of surface-roughened semipolar (11(2)over-bar2) GaN films by photochemical etching

作者：Jang Soohwan; Lee Sohyun; Baik Kwang Hyeon^*

来源：Japanese Journal of Applied Physics, 2017, 56(5): 051001.

DOI：10.7567/JJAP.56.051001

We studied the anisotropy of electrical conductivity in surface-roughened semipolar (11 (2) over bar2) GaN (s-GaN) films. Highly crystalline s-GaN films were obtained using asymmetric lateral epitaxy on oxide-patterned m-plane sapphire substrates. The in-plane structural anisotropy of the s-GaN films was confirmed by anisotropic peak broadening in X-ray rocking curves (XRC) with the in-beam orientations. The XRC full-width at half maximum (FWHM) values were measured to be 454 and 615 arcsec along the [(11 (2) over bar3)](GaN) and [1 (1) over bar 00](GaN) directions, respectively. The s-GaN surface was roughened using photo-chemical etching, and the electrical anisotropy was then investigated as a function of azimuth angles with the transmission line method. The Ohmic contact properties on the roughened s-GaN surface did not depend on the azimuth angle or annealing temperatures between 750 and 950 degrees C. The sheet resistances parallel to the [1 (1) over bar 00](GaN) direction on roughened s-GaN were found to be approximately half of the resistance parallel to the [11 (2) over bar3](GaN) direction, showing that anisotropic electrical conductivity is maintained for surface-roughened s-GaN due to charged carrier scattering induced by basal-plane stacking faults.

• 出版日期2017-5