Analyses of intrinsic magnetoelectric properties in spin-valve-type tunnel junctions with high magnetoresistance and low resistance

作者：Han XF^*; Yu ACC; Oogane M; Murai J; Daibou T; Miyazaki T

来源：Physical Review B, 2001, 63(22): 224404.

DOI：10.1103/PhysRevB.63.224404

A series of experimental data was obtained systematically for a spin-valve-type tunnel junction of Ta (5 nm)/Ni79Fe21 (3 nm)/Cu (20 nm)/Ni79Fe21 (3 nm)/Ir22Mn78 (10 nm)/Co75Fe25 (4 nm)/Al (0.8 nm)-oxide/ Co75Fe25 (4 nm)/Ni79Fe21 (20 nm)/Ta (5 nm). Analyses of (i) temperature dependence of tunnel magnetoresistance (TMR) ratio and resistance from 4.2 K to room temperature, (ii) applied de bias-voltage dependence of TMR ratio and resistance at 6.0 K and room temperature, and (iii) tunnel current I and dynamic conductance (dI/dV) as functions of de bias voltage at 6.0 K were carried out. High-TMR ratio of 64.7% at 4.2 K and 44.2% at room temperature were observed for this junction after annealing at 300 degreesC for an hour. An anisotropic wavelength cutoff energy of spin-wave spectrum in magnetic tunnel junctions, which is essential for self-consistent calculations. was suggested based on a series of inelastic electron tunnel spectra obtained. The main intrinsic magnetoelectric properties in such spin-valve-type tunnel junction with high magnetoresistance and low resistance can be evaluated based on the magnon-assisted inelastic excitation model and theory.

• 出版日期2001-6-1