Nanocrystalline FeAl intermetallics obtained in mechanically alloyed Fe50Al40Ni10 powder

作者：Hadef F^*; Otmani A; Djekoun A; Greneche J M

来源：Superlattices and Microstructures, 2011, 49(6): 654-665.

DOI：10.1016/j.spmi.2011.04.003

• Nanostructured materials
• Mechanical alloying
• Order-disorder effects
• X-ray diffraction
• Fe-57 Mossbauer spectroscopy

B2-Fe47Al53 intermetallics has been produced by mechanical alloying in a planetary ball mill, using elemental Fe, Al and Ni powder mixture. The microstructural and magnetic properties of the mechanically alloyed Fe50Al40Ni10 powdered samples were investigated by X-ray diffraction and Fe-57 Mossbauer spectrometry at 300 and 77 K. As resulted from the X-ray diffraction studies, the ordered B2 structure was formed in the Fe50Al40Ni10 powder, together with the bcc alpha(i)-Fe(Al, Ni) (i = 1,2) solid solutions. Further milling led to a partial disordering of B2-Fe47Al53; it has undergone an order-disorder transition which is characterized by an expansion of the volume Delta a(0) (lattice disorder) and a magnetic transition from the paramagnetic to ferromagnetic state which is characterized by strong ferromagnetic interactions in the alloy. The nanocrystalline bcc alpha(i)-Fe(Al, Ni) solid solution was ferromagnetic with a mean crystallite size of 6 nm.

• 出版日期2011-6