A Processing Map for Hot Deformation of an Ultrafine-Grained Aluminum-Magnesium-Silicon Alloy Prepared by Mechanical Milling and Hot Extrusion

作者：Asgharzadeh Hamed^*; Niazi Masoud Rahbar; Simchi Abdolreza

来源：Metallurgical and Materials Transactions A-Physical Metallurgy and Materials Science, 2015, 46A(12): 5900-5908.

DOI：10.1007/s11661-015-3162-3

Uniaxial compression test at different temperatures [573 K to 723 K (300 degrees C to 450 degrees C)] and strain rates (0.01 to 1 s(-1)) was employed to study the hot deformation behavior of an ultrafine-grained (UFG) Al6063 alloy prepared by the powder metallurgy route. The UFG alloy with an average grain size of similar to 0.3 mu m was prepared by mechanical milling of a gas-atomized aluminum alloy powder for 20 hours followed by hot powder extrusion at 723 K (450 degrees C). To elaborate the effect of grain size, the aluminum alloy powder was extruded without mechanical milling to attain a coarse-grained (CG) structure with an average grain size of about 2.2 mu m. By employing the dynamic materials model, processing maps for the hot deformation of the UFG and CG Al alloy were constructed. For investigation of microstructural evolutions and deformation instability occurring upon hot working, optical microscopy, scanning electron microscopy coupled with electron backscattered diffraction and transmission electron microscopy were utilized. It is shown that the grain refinement increases the deformation flow stress while reducing the strain hardening and power dissipation efficiency during the deformation process at the elevated temperatures. Restoration mechanisms, including dynamic recovery and recrystallization are demonstrated to control microstructural evolutions and thus the deformation behavior. Coarsening of the grain structure in the UFG alloy is illustrated, particularly when the deformation is performed at high temperatures and low strain rates. The manifestations of instability are observed in the form of cracking and void formation.

• 出版日期2015-12