Mixed-solvent thermal synthesis and magnetic properties of flower-like microstructured nickel

作者：Yimamu Aerpati; Beysen Sadeh^*; Peng Dengfeng; Aierken Yierpan

来源：Particuology, 2012, 10(3): 392-396.

DOI：10.1016/j.partic.2011.01.008

• Microstructure
• Magnetic materials
• Nanomaterials

Flower-like microstructured nickel was synthesized by a facile mixed-solvent thermal process. The structure, morphology, and magnetic properties of the reaction products were investigated, respectively, by X-ray diffraction (XRD), scanning electron microscopy (SEM), and vibrating sample magnetometry (VSM). The results showed that the products consisted of a face-centered cubic (fcc) structure with lattice constant of alpha = 3.524 angstrom. The average diameter of flower-like microstructured nickel was about 5 mu m and the thickness of a single flake was about 100 nm. Magnetic measurement showed that these powders exhibited ferromagnetic characteristics.

• 出版日期2012-6
• 单位新疆大学