Mini droplets to super droplets: evolution of self-assembled Au droplets on GaAs(111)B and (110)

作者：Sui Mao^*; Li Ming Yu; Kim Eun Soo; Lee Jihoon

来源：JOURNAL OF APPLIED CRYSTALLOGRAPHY, 2014, 47(2): 505-510.

DOI：10.1107/S1600576713034316

In this article, the effect of deposition amount on self-assembled Au droplets fabricated on GaAs(111)B and (110) is presented. The investigation is systematically performed by the variation of the Au deposition amount from 2 to 20 nm while fixing the other growth parameters such as annealing temperature and duration to clearly observe the effect. Under identical growth conditions, the self-assembled Au droplets show significantly different size and density depending on the amount of Au deposition: i.e. the average height varies by 436% from 21.8 to 95.5 nm and the average diameter swings by 827% from 52 to 430 nm, showing that the size increase is dominated by the lateral expansion. Meanwhile the average density varies by over two orders of magnitude from 1.24 x 10(8) to 4.48 x 10(10) cm(-2) on GaAs(111)B. With relatively low Au deposition amounts, below 3 nm, round dome-shaped mini Au droplets with high packing density can be fabricated, while super large Au droplets result with higher deposition amounts, above 10 nm, with a density two orders of magnitude lower. It is also found that the surface index has a minor effect on the fabrication of self-assembled Au droplets with the variation of deposition amount. The results are systematically analyzed and discussed in terms of atomic force microscopy and scanning electron microscopy images, line profiles, power spectrums, r.m.s. surface roughness, and size and density plots.

• 出版日期2014-4