First measurement of the nonlinear coefficient for Gd1-xLuxCa4O(BO3)(3) and Gd1-xScxCa4O(BO3)(3) crystals

作者：Andersen Martin Thalbitzer^*; Mortensen Jesper Liltorp; Germershausen Sven; Tidemand Lichtenberg Peter; Buchhave Preben; Gheorghe Lucian; Lupei Voicu; Loiseau Pascal; Aka Gerard

来源：Optics Express, 2007, 15(8): 4893-4901.

DOI：10.1364/OE.15.004893

The effective nonlinear coefficient and temperature acceptance bandwidth of three Lu and Sc co-doped GdCa4O(BO3) 3 type nonlinear crystals were measured. NCPM for SHG in to the blue-UV spectral region can be obtained by controlling the co-dopant concentration. Measurements were based on intra-cavity SHG of a CW Ti: Sapphire laser, and the effective nonlinear coefficients were found to be in the range of 0.5 to 0.6 pm/V for the three crystals used. The FWHM temperature acceptance bandwidth was measured to be more than 35 degrees C using a 6 mm long Gd0.871Lu0.129Ca4O(BO3)(3) crystal. A maximum of 115 mW at 407.3 nm in a single direction was measured using a 6.5 mm long Gd0.96Sc0.04Ca4O(BO3)(3) crystal.

• 出版日期2007-4-16