A Study of Aging Treatment on the Mg-10Li-0.5Zn Alloy

作者：Wang P C; Lin H C^*; Lin K M; Yeh M T; Lin C Y

来源：Materials Transactions, 2009, 50(9): 2259-2263.

DOI：10.2320/matertrans.M2009133

• magnesium-lithium alloy
• aging treatment
• precipitation hardening
• mechanical property

In this study, an aging treatment was performed to investigate the microstructures and mechanical properties of Mg-10Li-0.5Zn (LZ101) alloy. Experimental results show that the LZ101 Mg-Li alloy exhibits a dual-phase microstructure of alpha (HCP) and beta (BCC) phases, and has a good ductility. The 723 K solid-solution treated LZ101 Mg-Li alloy exhibits a single beta structure and produces alpha precipitates after natural and artificial aging. The solid-solution treated specimen has lower mechanical strength and higher elongation than the as-extruded one. The aged specimens exhibit a typical behaviour of precipitation hardening. The maximum tensile strength can reach 188 MPa, 180 MPa and 173 MPa, corresponding to the natural aging of 345.6 ks, 423 K aging of 21.6 ks and 523 K aging of 10.8 ks. [doi:10.2320/matertrans.M2009133]

• 出版日期2009-9