Al-H2O2 Semi-fuel Cell Using Ni Foam Supported NiCo2O4 Nanowire Arrays as Cathode

作者：Tian Yong Mei; Lei Ting; Wang Gui Ling^*; Cao Dian Xue

来源：Chemical Journal of Chinese Universities, 2011, 32(10): 2382-2386.

• Ni foam supported NiCo2O4 nanowire array
• Al-H2O2 semi-fuel cell
• Cathode catalyst

A Al-H2O2 semi-fuel cell using Ni foam supported NiCo2O4 nanowire arrays as cathode was reported. Ni foam supported-NiCo2O4 nanowire arrays were prepared by a template-free growth method, and demonstrated that NiCo2O4 nanowires grow almost vertically from the surface of foamed Ni substrate by scanning electron microscopy(SEM). The effects of concentrations of H2O2, flow rate of electrolyte as well as operation temperature on the cell performance were investigated. The cell exhibited an open circuit voltage of about 1.40 V; peak power densities of 79 and 120 mW/cm(2) at current densities of 98 and 172 mA/cm(2) and a cell voltage of 0.80 V and 0.70 V operating at room temperature and 320 K, respectively, using aluminium sheet as anode fuel and 0.6 mol/L H2O2 as oxidant. The current density at 0.7 V and voltage 75 mA/cm(2) remained nearly constant within a 5000 s test period, the Ni foam supported NiCo2O4 nanowire arrays electrode exhibits superior activity, stability, and mass transport property for H2O2 electroreduction.

• 出版日期2011-10-10
• 单位黑龙江大学; 哈尔滨工程大学