A novel tunable color emitting phosphor Sr3YLi(PO4)(3)F:Eu2+, Mn2+ for near-UV white LEDs based on the energy transfer from Eu2+ to Mn2+

作者：Lv, Yang; Jin, Yahong^*; Wang, Chuanlong; Ju, Guifang; Chen, Li; Hu, Yihua^*

来源：Journal of Materials Science: Materials in Electronics , 2017, 28(24): 19139-19147.

DOI：10.1007/s10854-017-7870-x

• SINGLE-PHASE
• LUMINESCENCE PROPERTIES
• CRYSTAL-STRUCTURE
• SILICATE GLASS
• LIGHT
• EMISSION
• BAND

Novel Eu2+ and Mn2+ doped fluorapatite-type Sr3YLi(PO4)(3)F powder materials have been synthesized via high temperature solid state reaction. The samples are characterized by X-ray diffraction (XRD), scanning electric microscopy (SEM), photoluminescence (PL) and photoluminescence excitation (PLE) spectra. Eu2+ single doped Sr3YLi(PO4)(3)F host displays a blue emission ranging from 400 to 550 nm centered at 439 nm, and exhibits a broad excitation band varying from 225 to 425 nm which matches with commercial n-UV LEDs (360-410 nm). Under near-UV light irradiation in the range from 270 to 410 nm, Eu2+ and Mn2+ co-doped Sr3YLi(PO4)(3)F phosphors show two emission bands centered at 439 and 565 nm, respectively. The relative intensity ratio of Eu2+ and Mn2+ can be changed by increasing the amount of Mn2+ ions, the emission color can be regulated from blue to white. The energy transfer process from Eu2+ to Mn2+ has been proved to the resonant type through the quadrupole-quadrupole interaction mechanism. It is important that the white light emission can be gained by modulating the relative contents of Eu2+ and Mn2+ ions in Sr3YLi(PO4)(3)F host. Base on the obtained results, the as-prepared phosphors might be applied as a candidate for white LEDs.

• 出版日期2017-12
• 单位广东工业大学