Size-Dependent Physical and Electrochemical Properties of Two-Dimensional MXene Flakes

作者：Maleski Kathleen; Ren Chang E; Zhao Meng Qjang; Anasori Babak; Gogotsi Yury^*

来源：ACS Applied Materials & Interfaces, 2018, 10(29): 24491-24498.

DOI：10.1021/acsami.8b04662

• two-dimensional material
• MXene
• flake size
• sonication
• density gradient centrifugation

Two-dimensional (2D) particles, including transition metal carbides (MXenes), often exhibit large lateral-size polydispersity in delaminated colloidal solutions. This heterogeneity results in challenges when conducting fundamental studies, such as investigating correlations between properties and the 2D flake size. To resolve this challenge, we have developed solution-processable techniques to control and sort 2D titanium carbide (Ti3C2Tx) MXene flakes after synthesis based on sonication and density gradient centrifugation, respectively. By tuning the sonication conditions, Ti3C2Tx flakes with varied lateral sizes, ranging from 0.1 to similar to 5 mu m, can be obtained. Furthermore, density gradient centrifugation was used to sort Ti3C2Tx flakes with different lateral sizes into more monodisperse fractions. These processing techniques allow for the characterization of size-dependent optical and electronic properties by measuring the absorption spectra and film conductivity, respectively. Additionally, by testing the material as electrochemical capacitor electrodes, we show the Ti3C2Tx flake-size dependence of electrochemical performance. Ti3C2Tx films made of flakes with lateral sizes of similar to 1 mu m showed the best capacitance of 290 F/g at 2 mV/s and rate performance with 200 F/g at 1000 mV/s. The work provides a general methodology which can be followed to control the size of MXenes and other 2D materials for a variety of applications and fundamental size-dependent studies.

• 出版日期2018-7-25