摘要
Layers of b-oriented silicalite crystals formed on alumina substrates were characterized by SEM and AFM. At short synthesis times, small 10-40 nm nuclei were found on the surfaces of the alumina particles of the support and also on the faces of well developed silicalite crystals. After a certain period of time, these nuclei are dissolved or incorporated into the growing crystals and only crystal growth can be observed. Large silicalite crystals (up to 3 mm in size) were also synthesized as a way to obtain a silicalite standard. The nanostructure of the nuclei above mentioned revealed by AFM was in agreement with that of a well growth large silicalite crystal.