Adaptive wettability-enhanced surfaces ordered on molded etched substrates using shrink film

作者：Jayadev Shreshta^*; Pegan Jonathan; Dyer David; McLane Jolie; Lim Jessica; Khine Michelle

来源：Smart Materials and Structures, 2013, 22(1): 014014.

DOI：10.1088/0964-1726/22/1/014014

Superhydrophobic surfaces in nature exhibit desirable properties including self-cleaning, bacterial resistance, and flight efficiency. However, creating such intricate multi-scale features with conventional fabrication approaches is difficult, expensive, and not scalable. By patterning photoresist on pre-stressed shrink-wrap film, which contracts by 95% in surface area when heated, such features over large areas can be obtained easily. Photoresist serves as a dry etch mask to create complex and high-aspect ratio microstructures in the film. Using a double-shrink process, we introduce adaptive wettability-enhanced surfaces ordered on molded etched (AWESOME) substrates. We first create a mask out of the children's toy 'Shrinky-Dinks' by printing dots using a laserjet printer. Heating this thermoplastic sheet causes the printed dots to shrink to a fraction of their original size. We then lithographically transfer the inverse pattern onto photoresist-coated shrink-wrap polyolefin film. The film is then plasma etched. After shrinking, the film serves as a high-aspect ratio mold for polydimethylsiloxane, creating a superhydrophobic surface with water contact angles >150 degrees and sliding angles <10 degrees. We pattern a microarray of 'sticky' spots with a dramatically different sliding angle compared to that of the superhydrophobic region, enabling microtiter-plate type assays without the need for a well plate.

• 出版日期2013-1