Scale-up production of lightweight high-strength polystyrene/carbonaceous filler composite foams with high-performance electromagnetic interference shielding

作者：Min, Zhiyu; Yang, Hao; Chen, Feng^*; Kuang, Tairong^*

来源：Materials Letters, 2018, 230: 157-160.

DOI：10.1016/j.matlet.2018.07.094

• Porous materials
• Microstructure
• Electrical properties
• EMI shielding

Conductive polymer composite (CPC) foams have been considered as a promising electromagnetic interference (EMI) shielding materials because of the advantages of the lightweight, low-cost and easy preparation process. However, most of the currently reported CPC foams were prepared by batch foaming process. Insight of large-scale and low-cost production of CPC foams, we presented a feasible extrusion foaming strategy of polystyrene (PS) composites with micro-graphite (mGr) or multi-wall carbon nanotube (MWCNT) using supercritical carbon dioxide (Sc-CO2) as the physical blowing agent for EMI shielding application. The composite foams showed elongated cell morphology; meanwhile, the compressive strength and electrical conductivity were significantly increased. These composite foams presented a remarkable high performance of EMI shielding efficiency, corresponding average EMI SE of 22 dB and specific EMI SE of 92 dB/(g/cm(3)). In comparison between mGr and MWCNT, PS/mGr composite foams showed better EMI SE than that of PS/MWCNT composite foams at the same filler content due to the lower foam density of PS/mGr composite foams. Considering the feasible, large-scale and low-cost production process, these CPC foams are expected to apply in high performance EMI shielding areas.

• 出版日期2018-11-1
• 单位洛阳理工学院; 浙江工业大学; 华南理工大学