Ultralow Loading of Silver Nanoparticles on Mn2O3 Nanowires Derived with Molten Salts: A High-Efficiency Catalyst for the Oxidative Removal of Toluene

作者：Deng, Jiguang^*; He, Shengnan; Xie, Shaohua; Yang, Huanggen; Liu, Yuxi; Guo, Guangsheng; Dai, Hongxing

来源：Environmental Science & Technology, 2015, 49(18): 11089-11095.

DOI：10.1021/acs.est.5b02350

• LOW-TEMPERATURE OXIDATION
• CARBON-MONOXIDE
• ACTIVE CATALYSTS
• GOLD NANOPARTICLES
• PT/TIO2 CATALYST
• MANGANESE OXIDES
• MESOPOROUS CO3O4
• NANOCATALYSTS
• FORMALDEHYDE
• PERFORMANCE

Using a mixture of NaNO3 and NaF as molten salt and MnSO4 and AgNO3 as metal precursors, 0.13 wt % Ag/Mn2O3 nanowires (0.13Ag/Mn2O3-ms) were fabricated after calcination at 420 degrees C for 2 h. Compared to the counterparts derived via the impregnation and poly(vinyl alcohol)-protected reduction routes as well as the bulk Mn2O3-supported silver catalyst, 0.13Ag/Mn2O3-ms exhibited a much higher catalytic activity for toluene oxidation. At a toluene/oxygen molar ratio of 1/400 and a space velocity of 40 000 mL/(g h), toluene could be completely oxidized into CO2 and H2O at 220 degrees C over the 0.13Ag/Mn2O3-ms catalyst. Furthermore, the toluene consumption rate per gram of noble metal over 0.13Ag/Mn2O3-ms was dozens of times as high as that over the supported Au or AuPd alloy catalysts reported in our previous works. It is concluded that the excellent catalytic activity of 0.13Ag/Mn2O3-ms was associated with its high dispersion of silver nanoparticles on the surface of Mn2O3 nanowires and good low-temperature reducibility. Due to high efficiency, good stability, low cost, and convenient preparation, 0.13Ag/Mn2O3-ms is a promising catalyst for the practical removal of volatile organic compounds.