Microstructural model for hot strip rolling of high-strength low-alloy steels

作者：Militzer M^*; Hawbolt EB; Meadowcroft TR

来源：Metallurgical and Materials Transactions A-Physical Metallurgy and Materials Science, 2000, 31(4): 1247-1259.

DOI：10.1007/s11661-000-0120-4

The microstructural evolution during hot-strip rolling has been investigated in four commercial high-strength low-alloy (HSLA) steels and compared to that of a plain, low-carbon steel. The recrystallization rates decrease as the Nb microalloying content increases, leading to an increased potential to accumulate retained strain during the final rolling passes. The final microstructure and properties of the hot band primarily depend on the austenite decomposition and precipitation during run-out table cooling and coiling. A combined transformation-ferrite-grain-size model, which was developed for plain, low-carbon steels, can be applied to HSLA steels with some minor modifications. The effect of rolling under no-recrystallization conditions (controlled rolling) on the transformation kinetics and ferrite grain refinement has been evaluated for the Nb-containing steels; Precipitation of carbides, nitrides, and/or carbonitrides takes place primarily during coiling, and particle coarsening controls the associated strengthening effect. The microstructural model has been verified by comparison to structures produced in industrial coil samples.

• 出版日期2000-4