A simple route towards low-temperature processing of nanoporous thin films using UV-irradiation: Application for dye solar cells

作者:Tebby Zoe; Babot Odile; Michau Dominique; Hirsch Lionel; Carlos Luis; Toupance Thierry*
来源:Journal of Photochemistry and Photobiology A: Chemistry , 2009, 205(1): 70-76.
DOI:10.1016/j.jphotochem.2009.03.020

摘要

Fabrication of anatase TiO(2) porous films at low temperature was achieved by a very simple, straightforward and cheap method involving the connection of oxide particles by UV-irradiation in air. The novelty of the method relies on the direct UV-irradiation of oxide nanoparticles, Without the presence of any oxide precursor or any additional treatment to form the nanoparticulate film. As electrodes for dye solar cells (DSCs), the 1-3 mu m-thick films modified with Dyesol N3 dye showed high photovoltaic responses, a maximum overall energy conversion efficiency of 2.4-2.5% being measured under AM1.5 illumination at 100 and 140 mW cm(-2). This method was extended to other semi-conducting oxides such as SnO(2). Efficiencies as high as 1.8% and 1.5% were measured under AM1.5 illumination at 64 and 140 mW cm(-2), respectively. This approach draws new prospects in the field of plastic organic-inorganic hybrid devices.

  • 出版日期2009-6-10