Ultrasmall sub-5nm nanoparticles in carbon matrices are synthesized by a facile hydrothermal route. The morphology and structure of the prepared samples were characterized by transmission electron microscopy (TEM) and X-ray diffraction (XRD). The electrochemical performances were evaluated by galvanostatic cycling and cyclic voltammetry. It is found that among the three nanocomposites Sn/C-3 with Sn nanoparticles content of 20.9wt% shows the best rate performance and the highest discharge capacity. At the current density of 200 mA g(-1), it shows a high dicharge capacity of 851.8 mAh g(-1). Even when the current density is increased to 5000 mA g(-1), a high discharge capacity of 168.1 mAh g(-1) can still be obtained. This result indicates a potential suitability of fabricating Sn/C electrode with high electrochemical performance.