Effect of raw materials pretreated by physical grinding method on the sintering ability and microwave dielectric properties of Li2MgTiO4 ceramics

作者：Zhou, Huanfu^*; Tan, Xianghu; Chen, Xiuli; Ruan, Hong

来源：Journal of Alloys and Compounds, 2018, 731: 839-843.

DOI：10.1016/j.jallcom.2017.10.114

• Li2MgTiO4 ceramics
• Sintering ability
• Sintering temperature range

Li2MgTiO4-1 (abbreviated as LMT-1) ceramics were synthesized via the solid state reaction method using the pretreated raw materials. The unpretreated raw materials were used in the preparation of Li2MgTiO4-2 (abbreviated as LMT-2) ceramics. The particle size of LMT-1 powders is smaller and more uniform than that of LMT-2 powders and the porosity of LMT-1 ceramics is lower than that of LMT-2 ceramics. The microwave dielectric properties of LMT-1 ceramics keep a relatively stable value at a wide sintering temperature range. The slight fluctuation of sintering temperature will lead to great changes in the microwave dielectric properties of LMT-2 ceramics. The pretreatment of raw materials enhances the sintering ability and broadens the sintering temperature range of the Li2MgTiO4 ceramics.

• 单位
  桂林理工大学