Modification of poly(L-lactic acid) electrospun fibers and films with poly(propylene imine) dendrimer

作者：Khaliliazar Sh; Akbari S; Kish M H

来源：Applied Surface Science, 2016, 363: 593-603.

DOI：10.1016/j.apsusc.2015.12.070

• Polylactic acid
• Poly(propylene imine) dendrimer
• Electrospinning
• Aminolysis

Poly(L-lactic acid) (PLLA) electrospun fibers and films were modified with the second generation of poly(propylene imine) dendrimer (PPI-G(2)) by three different approaches, namely, sodium hydroxide hydrolysis, plasma treatment and direct application of PPI-G(2). For the first and the second approaches, PLLA was modified by sodium hydroxide hydrolysis or plasma treatment to produce carboxylic acid groups. Then, the carboxylic acid groups were activated by 1-ethyl 3 (3 dimethylaminopropyl) carbodiimide (EDAC) and N,N'-dicyclohexyl carbodiimide (DCC) as a hetero bi-functional cross-linker. The cross-linkers promoted the grafting of carboxylic acid groups on the modified PLLA with NH2 groups of PPI-G(2). In the third approach, the PPI-G(2) dendrimer was directly used as an aminolysis agent for the functionalization of PLLA in a one step process. FTIR analysis confirmed the presence of NH2 groups of PPI-G(2) on the modified PLLA samples, resulting from each one of the three modification methods. Studies by SEM shows bead free electrospun fibers. Also, FE-SEM shows nano-cracks on the surface of films after modification. Contact angle, drug release tests, antibacterial effects and the dying results confirmed that these functionalization methods increased hydrophilicity and reactive side-chains of PLLA in the wet chemical process resulted in providing host-guest properties on the PLLA surface for adsorbing various kinds of guest molecules.

• 出版日期2016-2-15