A new approach to improve the local compressive properties of PPDO self-expandable stent

作者：Zhao, Fan; Xue, Wen; Wang, Fujun^*; Yu, Chenglong; Xu, Haiyan; Hao, Yi; Wang, Lu^*

来源：Journal of the Mechanical Behavior of Biomedical Materials, 2017, 68: 318-326.

DOI：10.1016/j.jmbbm.2017.02.015

• Thermal treatment
• PPDO braiding stent
• Local compression
• Crystallinity
• Conformer entropy

The radial performance of bioabsorbable polymeric intravascular stents is extremely important in assessing the efficiency of these devices in expanding narrow lumen, reducing stent recoil, and recovering to their original states after suffering from pulsating pressure. However, these stents remain inferior to metallic stents. Several thermal treatment conditions (60 degrees C, 80 degrees C, and 100 degrees C for 1 h) were investigated to improve the characteristics of poly(p-dioxanone) (PPDO) self-expandable stents. The local compressive force, stiffness, and viscoelasticity of these stents were also evaluated. Wide-angle X-ray diffraction and different scanning calorimetry measurements were performed to evaluate the recrystalline and thermodynamic changes of molecular chains. The declining conformer entropy of PPDO monofilaments was examined via energy analysis. The untreated stents had compressive modules of 514.80 +/- 70.59 mN/mm, which was much higher than those of 80 degrees C and 100 degrees C treated stents (332.35 +/- 66.08 mN/mm and 394.31 +/- 64.71 mN/mm, respectively). Nevertheless, 100 degrees C annealing stents had less stress relaxation and prior elastic recovery rate of 82.32 +/- 3.43 mN and 92.55 +/- 1.61%, respectively, showing a much better shape stability than untreated stents (139.51 +/- 16.67 mN and 86.18 +/- 3.57%, respectively). These findings present important clinical implications in the stent manufacturing process and warrant further study to develop new bioabsorbable stents with outstanding clinical efficacy.

• 出版日期2017-4
• 单位东华大学