The effect of a detonation nanodiamond coating on the thermal decomposition properties of RDX explosives

作者：Tong Yi^*; Liu Rui; Zhang Tonglai

来源：Physical Chemistry Chemical Physics, 2014, 16(33): 17648-17657.

DOI：10.1039/c4cp02237h

A well-dispersed and uniformly shaped detonation nanodiamond (DND) was produced and coated over micron scale RDX in various amounts to form four kinds of DND coating composites (NDRs). In order to confirm the optimal coating amount and its effect on the thermal properties, the thermal decomposition and kinetics were studied by DSC, TG and DPTA techniques. The critical temperature of thermal explosion (T-b) and the self accelerating decomposition temperature (T-SADT) both exhibit an interesting volcano-shaped changing trend and rank in an increasing order of NDR4 < NDR1 < RDX < NDR3 < NDR2. This indicates that the DND coating amount, ranging from 1/7 to 1/5, provides NDRs with better thermal safety than RDX. The thermolytic kinetic parameters (E-a and A) and activation thermodynamic parameters (Delta S-not equal, Delta W-not equal and Delta G(not equal)) are sorted in the following order: NDR1 < NDR4 < NDR2 < NDR3. The gas emission and reaction rate constant of the initial thermal decomposition have the same order. The results show that the DND coating could improve the reactivity of the NDRs and the effect is proportional to the coating amount. However, excessive coating that is more than 1/3 conversely hinders decomposition and gas diffusion, like a layer of protective shell. The isoconversional activation energy (E-a) varies with the conversion extent (alpha) at the initial stage of alpha = 0.1-0.5, which indicates that the thermal decomposition of the NDRs is a multi-step process including the secondary reaction or catalytic reaction. However, the E-a values are almost independent of alpha when alpha = 0.6-0.9, with the mean values in an increasing order of NDR1 < NDR4 < NDR2 < NDR3.

• 出版日期2014-9-7
• 单位北京理工大学