Deinking of Different Furnishes of Recycled MOW, ONP, and OMG Pulps in Silicate-Free Conditions Using Organic Complex of PHASS

作者：Akbarpour Iman^*; Ghaffari Mansour; Ghasemian Ali

来源：BioResources, 2013, 8(1): 31-44.

• Chemical deinking
• Recycled papers
• Organic complex
• PHAAS
• Optical properties
• Physical properties

Sodium silicate causes problems in papermaking such as deposit formation, decreased retention, and lower sheet strength. Due to these problems, chemical deinking of different recycled papers furnishes including 100% ONP, 80% ONP, and 20% OMG, and a combination of 70% ONP/20% OMG/10% MOW was accomplished using an organic complexing agent which included poly-hydroxyl acrylic acid and sodium salt (PHAAS) in silicate-free conditions. PHAAS was utilized at four levels of 0.3, 0.5, 0.7, and 1% (based on oven-dry weight of recycled paper) rather than sodium silicate. The optical and physical properties of deinked pulp were compared to control pulp (conventional deinking containing 2% sodium silicate). The results showed that the paper brightness was improved and the yellowness, dirt count, and dirt area were decreased significantly by increasing PHAAS charge up to 0.9%. Also, in different recycled paper furnishes above mentioned, using different charges of PHAAS had different effects on paper opacity. Using different charges of PHAAS (especially 0.7 to 0.9%) decreased paper caliper, increased paper air resistance, increased freeness, and gave similar or slightly better paper tear indices. Differences of tear indices were not significant at confidence level of 99%. Based on the present research, the use of 0.7 to 0.9% PHAAS in place of sodium silicate is advisable because of the better quality of final papers compared to conventional deinking process.

• 出版日期2013