New route for high oxygen semi-permeation through surface-modified dense La1-xSrxFe1-yGdyO3-delta perovskite membranes

作者：Vivet A; Geffroy P M^*; Thune E; Bonhomme C; Rossignol F; Richet N; Chartier T

来源：Journal of Membrane Science, 2014, 454: 97-108.

DOI：10.1016/j.memsci.2013.11.038

• Perovskite membrane
• Oxygen semi-permeation
• Sol-gel
• Ultra-divided coating
• EISA process

La1-xSrxFe1-yGdyO3-delta perovskite membranes are promising candidates for catalytic membrane reactors applications due to their potential high oxygen semi-permeation fluxes and good chemical stability in working conditions. The oxygen flux through La1-xSrxFe1-yGdyO3-delta perovskite membranes is mainly governed by oxygen exchanges at the membrane surface. This work shows how to strongly increase such an oxygen flux while developing a dedicated ultra-divided surface coating. Such a coating is obtained by Following a route derived from sol-gel and allowing an elementary grain diameter control in the 5-10 nm range. In this way, the oxygen fluxes through the coated membrane can be increased of more than an order of magnitude in comparison to uncoated membranes. This paper clearly shows that the oxygen flux through the uncoated membrane is governed by oxygen surface exchange, while for coated membranes it is governed by a balance between surface exchange and bulk diffusion. Our surfacemodified dense La1-xSrxFe1-yGdyO3-delta membranes show good performance in long term in working conditions (high temperature and large oxygen partial pressure gradients).

• 出版日期2014-3-15