Simultaneous graft copolymerization of 2-hydroxyethyl methacrylate and acrylic acid onto polydimethylsiloxane surfaces using a two-step plasma treatment

作者：Karkhaneh A; Mirzadeh H^*; Ghaffariyeh A R

来源：Journal of Applied Polymer Science, 2007, 105(4): 2208-2217.

DOI：10.1002/app.26216

• two-step plasma treatment
• surface modification
• polydimetylsiloxane
• hydroxyethyl methacrylate
• acrylic acid
• graft copolymerization

Acrylic acid (AAc) and 2-hydroxyethyl methacrylate (HEMA) mixtures were simultaneously grafted onto the surfaces of polydimethylsiloxane (PDMS) films using a two-step oxygen plasma treatment (TSPT). The first step of this method includes: oxygen plasma pretreatment of the PDMS films, immersion in HEMA/AAc mixtures, removal from the mixtures, and drying. The second step was carried out by plasma copolymerization of preadsorbed reactive monomers on the surfaces of dried pretreated films. The effects of pretreatment and polymerization time length, monomer concentration, and ratio on peroxide formation and graft amount were studied. The films were characterized by attenuated total reflection Furrier transformer infrared (ATR-FTIR) spectroscopy, scanning electron microscopy (SEM), atomic force microscopy (AFM), zeta potential, surface tension, and water contact angle measurements. The ATR-FTIR spectrum of the modified film after alkaline treatment showed the two new characteristic bands of PHEMA and PAAc. Both increase the polar part of surface tension (7,) after grafting and the evaluation of surface charge at pH 1.8, 7, and 12 confirmed the presence of polar groups on the surface of grafted films with a mixture of HEMA/AAc. Morphological studies using both AFM and SEM evaluation illustrated various amounts of grafted copolymer on the surface of PDMS films.

• 出版日期2007-8-15