NO2 sensing properties of Cr2O3 highlighted by work function investigations

作者：Stanoiu A^*; Simion C E; Diamandescu L; Tarabasanu Mihaila D; Feder M

来源：Thin Solid Films, 2012, 522: 395-400.

DOI：10.1016/j.tsf.2012.09.003

• Chromium oxide
• Chemical sensors
• Surface reactivity
• Work function
• Kelvin Probe

Gas sensing peculiarities of chromiumoxide (Cr2O3) nanoparticles, obtained by hydrothermal reaction at moderate temperature and subsequent thermal annealing, were studied. The structure and morphology of the obtained Cr2O3 samples were investigated by X-ray diffraction and transmission electron microscopy techniques. Gas sensing measurements revealed their selective sensitivity to nitrogen dioxide (NO2) at 200 degrees C relative to carbon monoxide (CO), both in dry and humid air. Higher selectivity towards NO2 is attributed to the material surface reactivity even at low operating temperatures. This property was experimentally highlighted by work function changes, as a complementary investigation method to basic electrical resistance. Thus, it was observed that the surface reactivity of Cr2O3 (calcinated at 1000 degrees C) towards NO2 is higher compared to CO and less influenced by the relative humidity of the surrounding atmosphere. The present study reveals possible applications in the selective detection of NO2 based on Cr2O3.

• 出版日期2012-11-1