Short vegetal-fiber reinforced HDPE-A study of electron-beam radiation treatment effects on mechanical and morphological properties

作者：Ferreira Maiara S; Sartori Mariana N; Oliveira Rene R; Guven Olgun; Moura Esperidiana A B^*

来源：Applied Surface Science, 2014, 310: 325-330.

DOI：10.1016/j.apsusc.2014.03.076

• HDPE
• Piassava fiber
• Glycidyl methacrylate
• Irradiation
• SEM
• Mechanical properties

The effects of electron-beam radiation treatment on fiber-matrix adhesion and mechanical properties of short piassava fibers reinforced high density polyethylene (HDPE) matrix were studied. Glycidyl methacrylate (GMA) was added at 2.5% and 5.0% (on piassava fiber wt) as a cross-linking agent and the effects upon the properties of the resulting composites treated by electron-beam radiation were also examined. HDPE reinforced with short piassava fiber composites was prepared by melt-mixing processing, using a twin screw extruder machine. The materials were irradiated with 100 and 200 kGy using a 1.5 MeV electron beam accelerator, at room temperature in presence of air. Material samples were submitted to mechanical and thermo-mechanical tests and SEM analyses. Correlation between properties was discussed. The comparison of mechanical and thermo-mechanical properties of the composites showed that electron-beam radiation treatment produced a significant improvement in mechanical properties, when compared with the non-irradiated composite sample and neat HDPE. Scanning electron microscopy (SEM) studies of the composite failure surfaces indicated that there was an improved adhesion between fiber and matrix. Examination of the failure surfaces indicated dependence of the interfacial adhesion upon the radiation dose and GMA content. Better interfacial adhesion between fiber and HDPE matrix was observed for composites with 5.0% GMA addition and treated with electron-beam radiation dose of 200 kGy. It can be concluded that GMA addition followed by electron-beam irradiation treatment, at the doses studied in this work, effectively improved the HDPE properties and led to the obtaining of composite materials with superior properties suitable for several industrial applications.

• 出版日期2014-8-15