Alkaline anion exchange membranes based on KOH-treated multilayer graphene oxide

作者：Bayer Thomas; Cunning Benjamin V; Selyanchyn Roman; Daio Takeshi; Nishihara Masamichi; Fujikawa Shigenori; Sasaki Kazunari; Lyth Stephen M^*

来源：Journal of Membrane Science, 2016, 508: 51-61.

DOI：10.1016/j.memsci.2016.02.017

• Alkaline fuel cell
• Anion exchange membrane
• Fuel cells
• Graphene oxide
• Ionic conductivity

A novel class of alkaline anion exchange membrane (AAEM) is presented, in the form of KOH-modified multilayer graphene oxide paper (GO(KOH)). Such membranes can be easily fabricated at large scale with varying thickness using conventional filtration techniques, and have high tensile strength (24.5 MPa). However, a large degree of swelling is observed. SEM investigations show that the morphology of GO changes after KOH-treatment, whilst XPS measurements and XRD analysis confirm successful chemical modification. The hydrogen gas permeability is several orders of magnitude lower than conventional polymer-based ionomer membranes. The maximum anion conductivity is 6.1 mS/cm at 70 degrees C, and the dominant charge carrier is confirmed to be OH- by utilization of anion and proton-conducting blocking layers. The ion exchange capacity is 6.1 mmol/g, measured by titration. A water-mediated reverse Grotthuss-like mechanism is proposed as the main diffusion mode of OH- ions. Finally, a prototype AAEM fuel cell is fabricated using a GO(KOH) membrane, confirming the applicability to real systems.

• 出版日期2016-6-15