Activity of Ni/CeO2 catalyst for gasification of phenol in supercritical water

作者：Li, Bin; Zhang, Baohua; Guan, Qingqing^*; Chen, Shanshuai; Ning, Ping^*

来源：International Journal of Hydrogen Energy, 2018, 43(41): 19010-19018.

DOI：10.1016/j.ijhydene.2018.08.105

• Phenol
• Gasification
• Supercritical water
• Ni/CeO2

An effective Ni/CeO2 catalyst prepared by the polyol reduction method for degrading phenol into CH4, H2 and CO2 in supercritical water (SCW) was developed. About 80% carbon gasification efficiency can be achieved at 525 degrees C and 60 min with 5 wt% phenol, 0.098 kg/m3 water density and 0.5 g Ni/CeO2/g phenol catalyst, forming CH4 and H-2 as the main gaseous products. Comparison study indicated that the efficiency of present Ni/CeO2 catalyst was about 20% higher than that of a commercial catalyst, i.e., Ni/SiO2 Al2O3 from Sigma Aldrich with 65 wt%Ni, at a reaction conditions of 500 degrees C and 30 min. The characterization analyses of BET, TPR, XRD, XPS and TEM indicated that there was a NiCe alloy formed in Ni/CeO2, which could be important to enhance the activities of the carbon gasification efficiencies and gas yields. A kinetic modelings were conducted and the results showed that the lnA and the activation energy (Ea) of gasification were 7.1 +/- 0.5 and 58.1 +/- 3.2 kJ/mol for the gaseous product, and were 2.6 0.9 and Ea is 36.6 5.6 kJ/mol for the char formation, respectively. The present Ni-based-metal Ni/CeO2 catalyst is cheaper and has a potential application for the gasification to convert phenol into gases fuels in SCW process.

• 出版日期2018-10-11
• 单位昆明理工大学