摘要
In this work, we report on the photo-catalytic properties of TiO2-ITO nanocomposite deposited on low cost conventional clay ceramic substrates. The nanocomposite was formed by spraying a solution prepared from the P25 TiO2 powder (Degussa) mixed with an organometallic paste of a dissolved combination of indium and tin. A TiO2-ITO powder-like nanocomposite was prepared for X-ray diffraction (XRD) and transmission electron microscopy (TEM) characterization. The mean particle size of the TiO2-ITO nanocomposite was found to be larger than that of pure TiO2. The optical features of TiO2-ITO-based layers (deposited on glass substrates) were investigated using UV-vis spectroscopy. The TiO2-ITO nanocomposite deposited layers were found to have higher light absorption than the P25 TiO2 powder. The photo-catalytic properties of the TiO2-ITO nanocomposite (deposited on low cost clay ceramic substrates) were tested under solar irradiation using a well-known polluting dye. It was shown that the TiO2-ITO nanocomposite exhibits higher degradation rates towards the pollutant dye than the P25 TiO2 powder. The optical band gap of the TiO2-ITO nanocomposite (2.79 eV) was found to be lower than that of pure TiO2 (3.1 eV), while ITO (indium in oxide) has a band gap of about 4.2 eV. ITO was found to be entirely transparent to sun light, while it exhibits a slight photo-catalytic activity, signifying the possible existence of an indirect photo-catalysis phenomenon (sensitized semiconductor photocalysis) and potential degradation (oxidation) of the pollutant through electron transfer from the dye to conduction band of the semiconductor. All photo-catalytic activity results were discussed in light of the optical band gap of the various compounds.
- 出版日期2010-1-15