Ag-0-loaded brookite/anatase composite was prepared via an alkalescent hydrothermal process. The photocatalytic performance of as-prepared catalysts was evaluated in terms of the degradation of methyl orange (MO). The physical features of the catalysts were measured with XRD, BET and HRTEM techniques. The phase content of brookite and anatase in the TiO2 can be controlled by fixing the concentration of the electrolyte in the hydrothermal system. The as-formed Ag-0 clusters have an average diameter of ca. 1.5 nm and intersperse throughout the surface of both anatase nanoparticles and brookite nanorods. Ag-0 has an optimal loading dosage of 2.0 mol%, with which the photocatalytic degradation of MO are 4.82 and 2.28 times of that with Ag-0-free composite and P25 TiO2, respectively. The synergistic effect of hetero-junction in brookite/anatase composite and the schottky barrier at the interface of Ag-0 and TiO2 significantly improved the separation of the photogenerated electrons and holes under UV irradiation and thus resulted in a much enhanced photocatalytic reactivity towards the degradation of MO.
- 出版日期2011-9-1
- 单位华东理工大学