Layered hydroxyl sulfate: Controlled crystallization, structure analysis, and green derivation of multi-color luminescent (La,RE)2O2SO4 and (La,RE)2O2S phosphors (RE = Pr, Sm, Eu, Tb, and Dy)

作者：Wang, Xuejiao; Li, Ji-Guang^*; Molokeev, Maxim S.; Zhu, Qi; Li, Xiaodong; Sun, Xudong

来源：Chemical Engineering Journal, 2016, 302: 577-586.

DOI：10.1016/j.cej.2016.05.089

• Sulfate type layered rare earth hydroxide
• Photoluminescence
• Oxysulfate
• Oxysulfide

The two important groups of Ln(2)O(2)SO(4) and Ln(2)O(2)S compounds are traditionally synthesized with the involvements of environmentally harmful sulfur-containing reagents. We developed in this work a unique green approach for their synthesis, using Ln(2)(OH)(4)SO4 center dot 2H(2)O layered hydroxyl sulfate as the precursor (Ln-241 phase). Phase selective crystallization of La-241 under both atmospheric pressure and hydrothermal conditions was firstly optimized, followed by transformation into La2O2S and La2O2SO4 by controlled calcination. Rietveld structure refinement was performed for La-241, La(OH)SO4, La2O2SO4, and La2O2S, and the crystal structure and cell parameters of La-241 were originally reported. The photoluminescence performances of several important activators (Pr3+, Sm3+, Eu3+, Tb3+, and Dy3+) in the two hosts, in terms of excitation, emission, quantum yield, and color coordinates of emission, were thoroughly investigated, and multi-color luminescence including bright red, green, orange red, and yellow was obtained under ultraviolet excitation. Detailed investigations of Tb3+ photoluminescence revealed that the lack of D-5(3) emission in La2O2S and the gradual quenching of D-5(3) blue emission at a higher Tb3+ content (hence decreasing I-488/I-545 ratio and changing color coordinates) in La2O2SO4 were suggested to be due to thermal activation of the D-5(3) electrons into the conduction band and cross

• 出版日期2016-10-15
• 单位东北大学