An Orange-Light Emitting Garnet Phosphor: Tb3Ga5O12:Eu3+

作者：Sawada Kenji; Nakamura Toshihiro^*; Adachiz Sadao

来源：ECS Journal of Solid State Science and Technology, 2017, 6(8): R97-R104.

DOI：10.1149/2.0091708jss

Tb3Ga5O12:Eu3+ (TGG:Eu3+) orange-light emitting garnet phosphor was synthesized by the solid-state reaction (SSR) method and subsequent calcination at T-c = 800-1400 degrees C in air. The effects of the Eu3+ activator concentration in (Tb1-xEux)(3)Ga5O12 and calcination temperature (T-c) on the phosphor properties were studied in detail. The strongest Eu3+ luminescence was observed at x similar to 0.05 and at T-c = 1400 degrees C. An exponential dependence was inferred from the X-ray diffraction and photoluminescence (PL) intensities vs 1/T-c plots, yielding Ea similar to 1.3 eV and similar to 4.0 eV for a formation of the host lattice and an activation of the Eu3+ ions in the TGG host, respectively. The PL properties of the TGG:Eu3+ phosphor were investigated in detail using PL excitation (PLE) spectroscopy and PL decay measurements. The PLE and PL decay characteristics showed an evidence of the energy transfer from the TGG host (Tb3+) to Eu3+ by excitation at lambda(ex) <= 500 nm. The internal quantum efficiency upon excitation at lambda(ex) = 380 nm was similar to 61%. Lattice temperature dependence of the PL intensity at T = 20-450 K was also measured and successfully interpreted using the conventional quenching model. A comparative discussion was given on the structural and PL properties of the SSR-grown TGG:Eu3+ phosphor with those of the metal-organic decomposition-grown TGG:Eu3+ one.

• 出版日期2017