Commercial grade polyethylene is melt electrospun from a thin film of unconfined molten polymer on a heated, electrically-grounded plate. Under the influence of an applied electric field, the melt spontaneously forms fingering perturbations at the plate edge which then evolve into emitting fiber-forming jets. Jet-to-jet spacing (similar to 5 mm), which is dependent on the applied voltage amplitude, is in agreement with estimates from a simple theoretical treatment. The broad applicability of the approach is verified by spinning a second polymer -polycaprolactone. In both cases, the fabricated fibers are similar in quality to those obtained under needle melt electrospinning; however for this method, there are no nozzles to clog and an enhanced production rate up to 80 mg min(-1) is achieved from approximately 20-25 simultaneous parallel jets. The process of jet formation, effective flow rates, cone-jet diameters, as well as limits on jet density and differences with polymer type are compared with theoretical models. This particular approach allows facile, high throughput micro-and nano-fiber formation from a wide variety of thermoplastics and other high viscosity fluids without the use of solvents or the persistent issues of clogging and pumping that hamper traditional methods, resulting in mechanically strong meso-scale fibers highly desirable for industrial applications.
- 出版日期2014-12
- 单位江南大学