Densification behavior and mechanical properties of nanocrystalline TiC reinforced 316L stainless steel composite parts fabricated by selective laser melting

作者：Zhao Shuming; Shen Xianfeng^*; Yang Jialin; Teng Wenhua; Wang Yingying

来源：Optics and Laser Technology, 2018, 103: 239-250.

DOI：10.1016/j.optlastec.2018.01.005

• Selective laser melting
• 316L stainless steel
• Nano-TiC reinforcement
• Relative density
• Microhardness
• Tensile strength

Metal matrix composite parts produced using selective laser melting have superior mechanical properties to those produced using traditional powder metallurgy. In this study, nanocrystalline TiC reinforced 316L stainless steel composite parts were fabricated using selective laser melting, and the effects of the TiC mass fraction, particle size, and processing parameters on the relative density, microhardness, and mechanical properties of the TiC/316L composites were investigated. The results show that the relative density of the fabricated parts is related to the laser power and exposure time, and increases when these parameters are increased. The greater the mass fraction of nano-TiC added, the more severe the degree of spheroidization and the lower the density of the resulting material. The microhardness of the 316L stainless steel parts is enhanced by the nano-TiC particles, and increases with increasing nano-TiC mass fraction. The tensile strength is improved with longer exposure time and with the addition of 2 wt% nano-TiC particles. Compared with pure 3161, the microhardness of the TiC/316L composite parts fabricated with 2 wt% 40 nm TiC enhanced from HV0.3 = 219.1 to 277.6, and the ultimate tensile strength significantly increased from 627.5 to 748.6 MPa. The strengthening mechanism of TiC particles is the refinement of the grain size of the 316L matrix, and the greater amount of TiC particles added, the better the grain refinement of 316L.

• 出版日期2018-7
• 单位中国工程物理研究院