Delamination and restacking of a layered double hydroxide with nitrate as counter anion

作者：Wu QL; Olafsen A; Vistad OB; Roots J; Norby P^*

来源：Journal of Materials Chemistry, 2005, 15(44): 4695-4700.

DOI：10.1039/b511184f

A layered double hydroxide (LDH) with nitrate as the counter anion (LDH- NO3 with Mg/Al = 3) was, for the first time, successfully delaminated in formamide under ultrasonic treatment. Atomic force microscopy (AFM) images showed that a large part of the LDH was delaminated into single and double brucite layers (0.7 - 1.4 nm in thickness). The nano-sheets had disk- like shapes with a diameter of ca. 20-40 nm. Findings from AFM were in good agreement with the average hydrodynamic diameter determined using dynamic light scattering. Powder X-ray diffraction pattern of LDH dispersed in formamide also confirmed that LDH-NO3 was exfoliated. The dispersions of LDH in formamide were stable and transparent up to a concentration of 40 g L-1. However, formation of transparent gels was observed at concentrations higher than 5 g L-1. Delaminated LDH could be restacked by adding sodium carbonate or ethanol.

• 出版日期2005