A vanadium dioxide (VO2) thin film was prepared on an Al-doped ZnO (AZO) conductive glass substrate by DC magnetron sputtering and a post-annealing process. The AZO/VO2/AZO sandwiched structure was fabricated on the VO2/AZO composite film using photolithography and a chemical etching process. The composition, microstructure and optical properties of the VO2/AZO composite film were tested. The results showed that the VO2/AZO composite film was poly-crystalline and the AZO layer did not change the preferred growth orientation of VO2. When the voltage was applied on both of the transparent conductive layers of the AZO/VO2/AZO sandwiched structure, an abrupt change in the current was observed at different temperatures. The temperature dependence of I-V characteristic curves for the AZO/VO2/AZO sandwiched structure was analyzed. The phase transition voltage value is 7.5 V at 20 degrees C and decreases with increasing temperature.