A hybrid damage assessment for E-and S-glass reinforced laminated composite structures under in-plane shear loading

作者：Yilmaz C; Akalin C; Gunal I; Celik H; Buyuk Murat; Suleman A; Yildiz M^*

来源：Composite Structures, 2018, 186: 347-354.

DOI：10.1016/j.compstruct.2017.12.023

• Shear modulus
• Reduction
• Iosipescu test
• Laminated composites

Micro-damage initiation and accumulation in two different Glass Fiber Reinforced -E-glass and S-glass-Laminated Composite Structures (LCS) subjected to in-plane shear stressing are monitored with Acoustic Emission (AE) and thermography methods. AE signals caused by micro-damage formation are graphed as a scatter plot of Weighted Peak Frequency (WPF) versus Partial Power 2 (PP2) features and clustered using the K-means algorithm with Bray Curtis dissimilarity function thus resulting in three different well-separated clusters. Each of these clusters corresponds to different micro damages, i.e., transverse cracks, delaminations, or fiber ruptures. It is observed that the E-glass reinforced LCS has higher numbers of AE hits. Thus, the total amount of micro-damage incurred as well as the average temperature change measured by thermography is higher for the E-glass reinforced LCS. It is shown that due to the curing induced residual tensile stress in E-glass reinforced LCS, the initial formation of delamination in E-glass reinforced LCS starts at higher load level. Under the applied shear load, a significant reduction in in-plane shear modulus is observed both for the E-glass and S-glass-reinforced LCS where the E-glass reinforced LCS shows greater reduction. The decrease in in-plane shear modulus is attributed to micro-damage accumulated in the LCS.

• 出版日期2018-2-15