NO2 Gas Sensing Properties of ZnO/Single-Wall Carbon Nanotube Composites

作者：Albiss Borhan A^*; Sakhaneh Wassef A; Jumah Inshad; Obaidat Ihab M

来源：IEEE Sensors Journal, 2010, 10(12): 1807-1812.

DOI：10.1109/JSEN.2010.2049739

• Temperature sensors
• Zinc oxide
• Temperature measurement
• Electron tubes
• Resistance
• Gas detectors

Networks of ZnO/single-wall carbon nanotube (ZnO/SWNT) composites were investigated as resistive gas sensors for NO2 detection. Sensor films were spin coated on sapphire substrates. Sensors' response, in dry air and in NO2 atmosphere, was measured by resistance measurements in the temperature range from 25 to 300 degrees C and gas concentration from 1 to 1000 ppm. At room temperature, ZnO/SWNT composites with equal weight ratio have shown quite high sensitivity to NO2 concentrations as low as 1 ppm. Significant increase in the sensitivity of the composite at higher temperatures up to 300 degrees C compared to that of ZnO free SWNTs. All tested sensors exhibited high stability and relatively low response and recovery times. The highest response values of the composite were obtained at temperatures ranging between 100 degrees C and 300 degrees C and gas concentrations higher that 50 ppm. For all gas concentrations, the ZnO/SWNT sensor shows much better performance at temperatures higher than 100 degrees C compared to the SWNT sensor. Our results revealed that the measured sensitivity upon exposure to NO2 strongly depends on the microstructure and the preparation conditions of the composite material. The gas detection mechanisms along with the optimal gas sensing parameters were discussed.

• 出版日期2010-12