Alkaline Activation of Ceramic Waste Materials

作者：Reig L^*; Tashima M M; Soriano L; Borrachero M V; Monzo J; Paya J

来源：Waste and Biomass Valorization, 2013, 4(4): 729-736.

DOI：10.1007/s12649-013-9197-z

• Ceramic waste
• Waste management
• Alkaline activation
• Compressive strength

Ceramic materials represent around 45 % of construction and demolition waste, and originate not only from the building process, but also as rejected bricks and tiles from industry. Despite the fact that these wastes are mostly used as road sub-base or construction backfill materials, they can also be employed as supplementary cementitious materials, or even as raw material for alkali-activated binders. This research aimed to investigate the properties and microstructure of alkali-activated cement pastes and mortars produced from ceramic waste materials of various origins. Sodium hydroxide and sodium silicate were used to prepare the activating solution. The compressive strength of the developed mortars ranged between 22 and 41 MPa after 7 days of curing at 65 degrees C, depending on the sodium concentration in the solution and the water/binder ratio. These results demonstrate the possibility of using alkali-activated ceramic materials in building applications.

• 出版日期2013-12