摘要
The purpose of this study was nondecalcified histologic analysis of titanium implants modified by laser with and without hydroxyapatite. Implants with three modified surfaces were inserted into rabbit tibias: group 1, machined surface; group 2, irradiated (laser); and group 3, irradiated and hydroxyapatite coated (biomimetic method). The mean surface roughness (Ra) scores of groups 2 and 3 were higher than that of group 1. Bone-implant contact measurements at 30 and 60 days for groups 2 and 3 were higher than for group 1. Bone area at 30 and 60 days for group 2 was higher than for groups 1 and 3. Titanium implants modified by laser with and without hydroxyapatite exhibit increased early osseointegration.