An alternative solid-state method to prepare pyrochlore-free KTaO3 at low temperature

作者：Su Tingting; Jiang Heng^*; Gong Hong

来源：Journal of Solid State Chemistry, 2011, 184(9): 2601-2604.

DOI：10.1016/j.jssc.2011.07.044

• KTaO3
• Perovskite
• Pyrochlore-free
• Alternative solid-state method

Perovskite-type KTaO3 powder was synthesized by an alternative solid-state method at low temperature. Stoichiometric ammonium tantalum hydroxide, K2C2O4 and KF were mixed in water and then dried at room temperature. The crude product was formed by calcining the dried mixture at different temperatures. Pyrochlore-free KTaO3 powder was successfully synthesized after treating the crude product with water. KF plays an important role to inhibit the formation of pyrochlore K2Ta2O6 during the calcination process of ammonium tantalum hydroxide/K2C2O4/KF mixture. X-ray diffraction (XRD), scanning electron microscopy (SEM), Fourier-transform infrared (FTIR) spectroscopy, UV-vis diffuse reflectance (UV-vis) spectroscopy and thermogravimetric (TG) analysis were used to characterize the precursor compound and as-prepared samples. XRD results show that pyrochlore-free KTaO3 powder can be obtained at 600 degrees C. SEM results reveal that the as-prepared products are agglomerated and each of the agglomerations consists of many small grains with 10-30 nm in diameter.

• 出版日期2011-9
• 单位辽宁石油化工大学