alpha-Fe2O3 nanowires deposited diatomite: highly efficient absorbents for the removal of arsenic

作者:Du Yucheng*; Fan Haiguang; Wang Liping; Wang Jinshu; Wu Junshu; Dai Hongxing
来源:Journal of Materials Chemistry A, 2013, 1(26): 7729-7737.
DOI:10.1039/c3ta11124e

摘要

alpha-Fe2O3 nanowires deposited diatomite was prepared using a precipitation-deposition method with FeCl3 as metal source and (NH2)(2)CO aqueous solution as precipitating agent. Physicochemical properties of the samples were characterized by means of numerous techniques, and their efficiency for the removal of As(III) and As(V) was determined. It is found that the solution pH value, reaction temperature, reaction time, and FeCl3 concentration had effects on the alpha-Fe2O3 amount loaded on the diatomite. Parameters, such as adsorbent amount, adsorption time, adsorption temperature, pH value, and initial As(III) or As(V) concentration, could influence the As(III) or As(V) removal efficiency of the alpha-Fe2O3 nanowires/diatomite sample (prepared with a 8 wt% FeCl3 aqueous solution at pH = 4.5 and 50 degrees C for 35 h) for the removal of As(III) and As(V). Over the alpha-Fe2O3/diatomite sample at pH = 3.5, the maximal As(III) and As(V) adsorption capacities were 60.6 and 81.2 mg g(-1), and the maximal As(III) and As(V) removal efficiency was 99.98 and 100%, respectively. The Langmuir model was more suitable for the adsorption of As(V), whereas the Freundlich model was more suitable for the adsorption of As(III). The adsorption mechanism of the sample was also discussed.