Asymmetric supercapacitors based on carbon nanotubes@NiO ultrathin nanosheets core-shell composites and MOF-derived porous carbon polyhedrons with super-long cycle life

作者：Yi, Huan; Wang, Huanwen; Jing, Yuting; Peng, Tianquan; Wang, Xuefeng^*

来源：Journal of Power Sources, 2015, 285: 281-290.

DOI：10.1016/j.jpowsour.2015.03.106

• Carbon nanotube
• Nickel oxide
• Porous carbon
• Asymmetric supercapacitor

Aqueous electrolyte based asymmetric supercapacitors (ASCs) has recently attracted increasing interest by virtue of their operation voltage and high ionic conductivity. Herein, we developed a novel ASC based on carbon nanotubes@nickel oxide nanosheets (CNT@NiO) core-shell composites as positive electrode and porous carbon polyhedrons (PCPs) as negative electrode in aqueous KOH solution as electrolyte. The CNT@NiO core-shell hybrids were prepared through a facile chemical bath deposition method followed by thermal annealing, while PCPs were obtained by direct carbonization of Zn-based metal-organic frameworks (MOFs). Owing to their unique microstructures, outstanding electrochemical properties have been achieved in three-electrode configuration, e.g., 996 F g(-1) at 1 A g(-1), 500 at 20 A g(-1) for the CNT@NiO electrode within 0-0.5 V window, and 245 F g(-1) at 1 A g(-1) for the PCPs electrode within -1 -0 V Resulting from these merits, the as-fabricated CNT@NiO//PCPs ASC exhibits maximum energy density of 25.4 Wh kg(-1) at a power density of 400 W kg(-1) and even remains 9.8 Wh kg(-1) at 16,000 W kg-1 (a full charge-discharge within 4.4 s) in the wide voltage region of 0-1.6 V. More importantly, the CNT@NiO//PCP5 asymmetric supercapacitor shows ultralong cycling stability, with 93% capacitance retention after 10,000 cycles.

• 出版日期2015-7-1
• 单位同济大学