Ultraviolet Irradiation Effects on luminescent Centres in Bismuth-Doped and Bismuth-Erbium Co-Doped Optical Fibers via Atomic Layer Deposition

作者：Uddin, Rahim; Wen, Jianxiang^*; He, Tao; Pang, Fufei; Chen, Zhenyi; Wang, Tingyun^*

来源：Electronics, 2018, 7(10): 259.

DOI：10.3390/electronics7100259

• UV irradiation
• luminescent centres
• bismuth ions
• two-photon process

The effects of ultraviolet irradiation on luminescent centres in bismuth-doped (BDF) and bismuth/erbium co-doped (BEDF) optical fibers were examined in this study. The fibers were fabricated by modified chemical vapor deposition combining with atomic layer deposition method. The fibers were exposed to irradiation from a 193 nm pulsed wave argon fluoride laser, and an 830 nm wavelength laser diode pump source was employed for excitation. The experimental results showed that, for the BDF, the transmission loss was slightly reduced and the luminescence intensity was increased at the bismuth-related active aluminum centre (BAC-Al). Then, for the BEDF, the transmission loss was increased a little and the luminescence intensity was also increased at the BAC-Al centre. However, the luminescence intensity was decreased at approximately 1420 nm of the bismuth-related active silica centre (BAC-Si) for all fiber samples. One possible formation mechanism for luminescence intensity changes was probably associated with the valence state transfer of bismuth ions. The other possible mechanism was that the ArF-driven two-photon process caused luminescence changes in BAC-Al and BAC-Si. It was very important to reveal nature of luminescence properties of Bi-doped and Bi/Er co-doped optical fiber.

• 出版日期2018-10
• 单位上海大学