Al-2024 alloy was reinforced with silicon carbide nanoparticles (SiCNP), whose concentration was varied in the range from 0 to 5 wt.%; some composites were synthesized with the mechanical milling (MM) process. Structure and microstructure of the consolidated samples were studied by X-ray diffraction and transmission electron microscopy, while mechanical properties were investigated by compressive tests and hardness measurements. The microstructural evidence shows that SiCNP were homogeneously dispersed into the Al-2024 alloy using high-energy MM after 2 h of processing. On the other hand, an increase of the mechanical properties (yield stress, maximum strength and hardness) was observed in the synthesized composites as a direct function of the SiCNP content. In this research several strengthening mechanisms were observed, but the main was the obstruction of dislocations movement by the addition of SiCNP.