Nanomechanical properties of hydroxyapatite (HAP) with DAB dendrimers (poly-propylene imine) coatings onto titanium surfaces

作者：Charitidis Costas A^*; Skarmoutsou Amalia; Tsetsekou Athena; Brasinika Despina; Tsiourvas Dimitris

来源：Materials Science and Engineering B-Solid State Materials for Advanced Technology, 2013, 178(7): 391-399.

DOI：10.1016/j.mseb.2013.01.002

• Hyhdroxyapatite
• Dendrimer
• Nanoindentation
• Plasticity index
• Wear resistance

Coatings of hydroxyapatite (HAP) nanorods onto titanium surfaces were synthesized with the aim to improve coatings%26apos; mechanical properties and adhesion to the substrate. The coatings are consisting of HAP nanorods synthesized in the presence of a cationic fourth generation diaminobutane poly(propylene imine) dendrimer (DAB) bearing 32 amine end groups employing varying calcium: dendrimer ratios and varying hydrothermal treatments. The quality, surface morphology and structure of the coatings were characterized with X-ray diffraction, thermogravimetric analysis, scanning electron microscopy and energy dispersive microanalysis. Wear resistance and adhesion properties of the coatings onto titanium substrates were studied through nanoindentation analysis. The experimental conditions, namely the calcium: dendrimer molar ratio and the hydrothermal treatment temperature were carefully selected: thus, it was possible to produce coatings of high hardness and elastic modulus values (ranging between 1-4.5 GPa and 40-150 GPa, respectively) and/or high wear resistance and plastic deformation values.

• 出版日期2013-4-20