High speed end milling of a zirconium alloy

作者：Hood Richard; Soo Sein Leung^*; Sage Colin; Carcass Phill

来源：CIRP Annals, 2015, 64(1): 105-108.

DOI：10.1016/j.cirp.2015.04.057

• Surface integrity
• Milling
• Zirconium

The paper details a comprehensive investigation into the machinability and surface integrity of Zircaloy-4 following end milling. Tool wear after machining for similar to 30 min at a cutting speed of 320 m/min was low, with surface roughness (Ra) values typically <0.6 mu m. No evidence of thermal damage was detected on any of the surface/subsurface cross-sections analysed, although adhesion/re-deposition and smeared material with a width of similar to 50 mu m was prevalent on the workpiece surface, particularly when operating at higher cutting speeds (320 m/min) and depths of cut (0.6 mm). Surface residual stresses were compressive up to a value of 120 MPa.

• 出版日期2015