Magnetostriction Behavior of Pseudobulk CoFeBSiNb(Ga) Systems

作者：Hosko J^*; Janotova I; Svec P; V****k G; Matko I; Janickovic D; Gemming T; Stoica M; Svec P Sr

来源：Journal of Superconductivity and Novel Magnetism, 2013, 26(4): 797-800.

DOI：10.1007/s10948-012-2036-9

• Ribbon
• Pseudobulk metallic glasses
• Planar flow casting
• Saturation magnetostriction

Co-based ferromagnetic amorphous systems prepared by rapid quenching are parts of a very interesting group of materials from the perspective of new magnetic application possibilities. Practical applications of amorphous metallic glasses are in some cases limited by the thickness of the ribbon. In the present contribution as-cast and after annealing Co-Fe-B-Si-Nb ribbons (monolayer), pseudobulk (bilayer, trilayer) materials with increased thickness in comparison with ribbons (monolayer) and Co-Fe-B-Si-Nb-Ga ribbon were investigated by measurements of magnetostriction lambda (s) . These materials were prepared by planar flow casting method (PFC) and modified PFC method with a single crucible which has two or three nozzles for preparation of pseudobulk samples, respectively. The field dependence of the parallel [lambda (par)(H)] and perpendicular [lambda (perp)(H)] magnetostrictions in the sample plane was measured at room temperature. These dependencies were used to calculate the values of saturation magnetostriction lambda (s) . Microstructure of the as-cast samples as well as annealed samples was investigated by X-ray diffraction (XRD), transmission electron microscopy (TEM) and high-resolution electron microscopy (HREM).

• 出版日期2013-4